Quick Details

  • Grade: 400 Series
  • Standard: ASTM, AISI, DIN, EN, GB, JIS
  • Length: customized
  • Thickness: 0.1- 16.0mm
  • Width: below 350mm
  • Place of Origin: Jiangsu, China (Mainland)
  • Brand Name: Changjiang
  • Model Number: AISI 416 / DIN 1.4005
  • Type: Plate
  • Application: automatic screw machine parts, valve components, pump shafts etc.
  • Certification: SGS
  • Dimensions: Customized
  • Reliable factory: Professional sales team

Packaging & Delivery

Packaging Details Seaworthy packing.
Delivery Time Within 15- 45 working days.

AISI 416 / DIN 1.4005 Stainless steel plates

 

416 Stainless Steel is a martensitic free machining grade of stainless that can be hardened by

heat treatment to achieve elevated strength and hardness.

Due to its low cost and ready machinability, 416 stainless steel is readily used in its highly tempered state.

It exhibits better machining characteristics than austenitic grades, however, sacrifices corrosion resistance.

Since stainless steel 416 is free of high sulfer content, it is not suitable for marine or any chloride exposure situations.

 

Best Stainless provides 416 stainless steel under the highest quality UNS S41600 and ASTM A582 standards.

416 SS can be utilized in a number of capacities and applications including, pump shafts, valve components, and

automatic screw machine parts. Stainless steel 416 is composed of carbon, chromium, manganese, phosphorous,

silicon, and sulfur.

 

Chemical composition ( % ) 

Carbon             0.150 max

Chromium       12.0- 14.0 

Manganese     1.250 max

Phosphorous  0.060 max

Silicon              1.00 max

Sulfur                0.150 max

Molybdenum   0.60 max

 

Applications 

A wide variety of screw machine parts including nuts, bolts, screws, gears and pinions, valve trim, shafts and axles. 

 

Machinability 

Speeds and feed comparable with those of some of the free machining carbon steels.

Good chip breakage. Material heat treated at 200°F and cold drawn will give best results.  

 

Welding 

Welding of any type is not recommended, as the high sulfur content creates porosity.  

 

Hot working 

All hot work procedures should commence following uniform heating to 2100-2250°F (1149-1232°c).

Hot work below 1700°F (927°c) may result in cracking.  

 

Cold working 

This alloy will accept only minor cold working. Severe deformation will result in cracking.  

 

Annealing 

1200-1400°F (650-760°c), air cool. For maximum softness, 1500-1650°F (816-900°c), furnace cool.  

 

Tempering  

Temper to achieve properties desired. Avoid tempering in the range of 750-1050°F (399-566°c) to avoid a decrease in

impact strength and corrosion resistance.  

 

Hardening  

Soak at 1700-1850°F (927-1010°c) oil quench. 

 

Physical data 

Density (lb / cu. in.)       0.28

Specific Gravity               7.7

Specific Heat (Btu/lb/Deg °F - [32-212 Deg °F])                0.11

Electrical Resistivity (microhm-cm (at 68 Deg °F))         343

Modulus of Elasticity Tension                                            29

 

Contact Ahonest sales to discuss more

Follow us on Linkedin & Facebook

Online Skype: paul_luhongxiang

Whatsapp: 0086 15190257143

Transaction History of the Supplier

Below is the information about the supplier's transactions conducted via Alibaba.com. If you require further details regarding the transaction data, please contact the supplier directly.

Transaction Overview

Transactions

Transaction Details

This supplier has completedtransactions with buyers from .

Shipping Destination
Transaction Value
Transaction Date
Email to this supplier
China (Mainland) | Manufacturer, Trading Company
Transaction Level:
Supplier Assessments:
The supplier supports Trade Assurance – A free service that protects your orders from payment to delivery.
Supplier's Trade Assurance Limit: US $29,000
Learn More