Quick Details

  • Grade: 400 Series
  • Standard: ASTM, AISI, DIN, EN, GB, JIS
  • Length: cut to lengths, straightened
  • Thickness: 0.1mm ~
  • Width: below 2000mm
  • Place of Origin: Jiangsu, China (Mainland)
  • Brand Name: Changjiang
  • Model Number: W.-Nr. 1.4006 ( DIN X12Cr13 ), ASTM TYPE 410 / UNS S41000
  • Type: Plate
  • Application: Cutlery, steam and gas turbine blades and buckets, bushings etc.
  • Certification: SGS
  • Surface: 2B, No.1
  • Dimensions: Customized
  • Reliable factory: Professional sales team

Packaging & Delivery

Packaging Details Seaworthy packing.

Martensitic stainless steel plates W.-Nr. 1.4006 ( DIN X12Cr13 )

 

EN 1.4006, DIN X12Cr13, ASTM TYPE 410 / UNS S41000 is the basic martensitic stainless which will attain high mechanical properties after heat treatment.

It has good impact strength, corrosion and scaling resistance up to 1200°F (649°c).

 

Designations

AISI 410

JIS SUS410

GB 10Cr13 

EN 1.4006   DIN X12Cr13

UNS S41000 

 

Chemistry data ( in weight % )

Carbon           0.15 max

Chromium      11.5 - 13.5

Iron                Balance

Manganese    1.0 max

Phosphorus    0.04 max

Silicon           1.0 max

Sulphur          0.03 max  

 

Applications 

Cutlery, steam and gas turbine blades and buckets, bushings, valve components, fasteners, screens and kitchen utensils.

 

Machinability

Tough, draggy chips with heavy build-up. While this alloy can be machined in the annealed condition, it tends to perform

better in the cold drawn or heat treated condition.

 

Welding 

Most common methods of welding can be successfully employed with this alloy.

To reduce the chance of cracking, it is advisable to preheat the workpiece to 350-400°F (177-204°c).

Post-weld annealing is recommended to reattain maximum ductility.

Filler metal, when required, should be AWS E/ER 410.

 

Hot working 

2000-2200°F (1093-1204°c) is the proper hot work range.

Do not work this material below 1650°F (899°c).

 

Cold working 

Readily cold formed using most of the common practices.

 

Annealing 

1200-1400°F (649-760°c), followed by air cooling.

 

Tempering 

Temper for desired hardness, air or furnace cool.

 

Hardening 

1750-1850°F (954-1010°c), oil quench for maximum hardness.

 

Physical data 

Density (lb / cu. in.)   0.28

Specific Gravity  7.7

Specific Heat (Btu/lb/Deg °F - [32-212 Deg °F])   0.11

Electrical Resistivity (microhm-cm (at 68 Deg °F))   342

Melting Point (Deg °F)   2790

Modulus of Elasticity Tension   29 

 

We are looking forward to your enquiries.

Please call +86 151 9025 7143, skype: paul_luhongxiang or send an email to

export @ ahoneststeel dot com

Transaction History of the Supplier

Below is the information about the supplier's transactions conducted via Alibaba.com. If you require further details regarding the transaction data, please contact the supplier directly.

Transaction Overview

Transactions

Transaction Details

This supplier has completedtransactions with buyers from .

Shipping Destination
Transaction Value
Transaction Date
Email to this supplier
China (Mainland) | Manufacturer, Trading Company
Transaction Level:
Supplier Assessments:
The supplier supports Trade Assurance – A free service that protects your orders from payment to delivery.
Supplier's Trade Assurance Limit: US $29,000
Learn More